Resistance Wire/Heating Element/Fecral Alloy Wire/ Electric Heating Wire

• Customization: Available
• After-sales Service: Available
• Warranty: 3 Years
• Model NO.: INNOVAT
• Material: Fecral
• Cross Sectional Shape: Round
• Application: Construction Wire Mesh, Protecting Mesh, Fence Mesh, Filter, Cages
• Type: Flat Wire
• Wide in Width: 0.03mm-12mm
• Surface Treatment: Coated
• Metal Wire Drawing: Hot Drawing
• Status: Hard State
• Thickness: Metal Filament
• Ribbon: (0.05-0.35)*(0.5-6.0)mm
• Transport Package: Plywood Case
• Specification: 8-50mm
• Trademark: INNOVAT
• Origin: China
• HS Code: 7223000000
• Production Capacity: 5000

Product Description

FeCrAl alloy has the characteristic of high resistivity,low temperature resistance coefficient,high operating temperature,
good anti-oxidation and anti-corrosion under high temperature.It is widely used in industrial furnace, household appliances, industry furnace, metallurgy, machinery, aircraft, 
automotive and other industries producing heating elements and resistance elements.

Size Range
Wire	dia 0.03-7.5mm
	dia 8.0-12.0mm
Ribbon	(0.05-0.35)*(0.5-6.0)mm
Strip	(0.50-2.5)*(5-180)mm
Rod	8-50mm

.....................................................................................................................................................................................................................................

Performance\ material		1Cr13Al4	0Cr25Al5	0Cr21Al6	0Cr23Al5	0Cr21Al4	0Cr21Al6Nb
Composition	Cr	12-15	23-26	19-22	20.5-23.5	18-21	21-23
	Al	4-6	4.5-6.5	5-7	4.2-5.3	3-4.2	5-7
	Fe	rest	rest	rest	rest	rest	rest
Maximum temperatureºC		950	1250	1250	1250	1100	1350
Meltiing point ºC		1450	1500	1500	1500	1500	1510
Density g/cm3		7.4	7.1	7.16	7.25	7.35	7.1
Hardness(H.B.)		200-260	200-260	200-260	200-260	200-260	200-260
Tensile strength(N/mm2)		580-680	630-780	630-780	630-780	600-700	650-800
Variation of area(%)		65-75	60-75	65-75	65-75	65-75	65-75
Resistivity  at 20ºC((μΩ·m)		1.25	1.42	1.42	1.35	1.23	1.45
Elongation at rupture		≥16	≥12	≥12	≥12	≥12	≥12
Coefficient of lines expansion(αx10-6ºC)		15.4	16	14.7	15	13.5	16
Thermal conductivity KJ/m.hºC		52.7	46.1	63.2	60.2	46.9	46.1
continuous servicetime(Hours/ºC)		__	≥80/1300	≥80/1300	≥80/1300	≥80/1300	≥50/1300
Micrographic structure		Ferrite	Ferrite	Ferrite	Ferrite	Ferrite	Ferrite
Magnetic properties		magnetic	magnetic	magnetic	magnetic	magnetic	magnetic